| Grades | Total amine value mgKOH/g |
Relative density (20℃)g/ml |
Viscosity (mPa·s@25℃） | Water（%） | solid content（%） | Gel time(mins)/ reaction with HT-100 (min,25±2℃，RH55±10%) |
Tack free time(mins)/（reaction with HT-100,film thickness 100μm；25±2℃，RH55±10%） | Characteristics and applications |
|---|---|---|---|---|---|---|---|---|
| W2850 | 180-200 | 1.05±0.02 | 80-150 | ＜0.15 | 97±2 | 100-110 | 50 | Low reactivity, adjustable,suitable for anti-corrosion, floor, adhesive, etc. |
| W520 | 183-193 | 1.06±0.02 | 800-2000 | ＜0.15 | 97±2 | 450-510 | 450 | Low reactivity, excellent leveling, suitable for floor, anti-corrosion, decorative paint, wind turbine blade, etc. |
| W420 | 190-203 | 1.06±0.02 | 800-1500 | ＜0.15 | 97±2 | 70-80 | 28 | High reactive activity, fast tack free speed, suitable for waterproofing, protective, adhesive, etc. |
| W330 | 165-175 | 1.06±0.02 | 200-600 | ＜0.15 | 97±2 | 80-85 | 28 | The product has low viscosity and moderate reactivity, and is suitable for solvent-free floor, waterproof coating, adhesive, etc. |
| W220 | 230-249 | 1.05±0.03 | 50-100 | ＜0.15 | 97±2 | 1-2 | − | High reactivity,fast tack free speed, can be used for fast adhesive, road marking paint,concrete sealing materials, etc. |
| W820 | 25-35 | 1.05±0.02 | 1000-2000 | ＜0.15 | 97±2 | —— | 90 | Low reactivity, suitable for waterproofing, floor coating, sealant, etc. |
| W523 | 183-193 | 1.06±0.02 | 800-2000 | ＜0.15 | 97±2 | 750-800 | 450 | Low reactivity, excellent leveling property, suitable for flooring, anti-corrosion, decorative paints, wind turbine blades, etc. |
| W423 | 190-203 | 1.06±0.02 | 800-1500 | ＜0.15 | 97±2 | 95-105 | 30 | High reactivity, fast tack free speed, suitable for waterproofing, anti-corrosion, adhesives, floor coatings, etc. |
| W2850H | 180-200 | 1.05±0.02 | 80-150 | ＜0.15 | 99.5±0.5 | 100-110 | 50 | Low free, high solid content, low odor, suitable for anti-corrosion, floor,wind turbine blade,adhesive, etc. |
| W520H | 188-196 | 1.06±0.02 | 1500-3000 | ＜0.15 | 99.5±0.5 | 450-510 | 450 | Low free, high solid content, low odor, the product can be used alone, suitable for floor, decorative paint, repair paint, etc. |
| W420H | 195-205 | 1.06±0.02 | 900-1800 | ＜0.15 | 99.5±0.5 | 80-90 | 26 | Low free, high solid content, low odor, suitable for waterproof repair, adhesive, wood paint, etc. |
| W330H | 165-175 | 1.06±0.02 | 300-800 | ＜0.15 | 99.5±0.5 | 80-85 | 28 | Low free, high solid content, low odor, can be used to make high elongation, high elasticity of the coating and adhesive materials |
| W523H | 188-196 | 1.06±0.02 | 1500-3000 | ＜0.15 | 99.5±0.5 | 750-800 | 450 | Low free, high solid content, low odor. The product can be used alone and is suitable for use in flooring, wind turbine blades, anti-corrosion, etc. |
| W423H | 195-205 | 1.06±0.02 | 900-1800 | ＜0.15 | 99.5±0.5 | 95-105 | 26 | Low free , high solid content, low odor. Suitable for waterproofing, anti-corrosion, adhesives, floor coatings, etc. |
| Aspartic polyurea tile grout raw material recommended solution |
|---|
| WS-G5401 | Total amine value mgKOH/g | Viscosity（Pa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications |
| 195±5 | 1500±500 | ＜0.1% | ＞99.0 | In the field of aspartic polyurea tile grout, at 25 ℃，50% RH, the working time for the product is 15-20 minutes, the trimming time is 2-3 hours, rapid curing. | |
| N6813 | NCO content（%） | Viscosity （Pa·s@25℃） | Water（%） | effective constituent（%） | |
| 13.5±0.5% | 3100±500 | — | ＞99% |
| WS-G5402 | Total amine value mgKOH/g | Viscosity（Pa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications |
| 185±5 | 800±300 | ＜0.1% | ＞99.0 | In the field of aspartic polyurea tile grout, at 25 ℃，50%RH,the working time for the product is 30-35 minutes, the trimming time is 6-7 hours, enough operation time, good flexibility. | |
| N5630 | NCO content（%） | Viscosity（Pa·s@25℃） | water（%） | effective constituent（%） | |
| 13.5±0.5% | 3100±500 | — | ＞99% |
| WS-G5405 | Total amine value mgKOH/g | Viscosity（Pa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications |
| 190±5 | 500±300 | ＜0.1% | ＞99.0 | In the field of aspartic polyurea tile grout, at 25 ℃，50%RH, the working time for the product is 20-25 minutes,the trimming time is 4-5h,the tensile strength can reach to 20Mpa. | |
| N5631 | NCO content（%） | Viscosity（Pa·s@25℃） | Water（%） | effective constituent（%） | |
| 14.5±0.5% | 2500±500 | — | ＞99% |
| WS-G5406 | Total amine value mgKOH/g | Viscosity （Pa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications |
| 170±5 | 2000±500 | ＜0.1% | ＞99.0 | In the field of aspartic polyurea tile grout, at 25 ℃，50% Rh, the working time for the product is 20-25 minutes,the trimming time is 4-5h,compare with the product WS-G5405+N5631, the adhension ability is improved. | |
| N5631 | NCO content（%） | Viscosity（Pa·s@25℃） | water（%） | effective constituent（%） | |
| 15.0±0.5% | 4500±500 | — | ＞99% |
| WS-G5408 | Total amine value mgKOH/g | Viscosity（Pa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications |
| 170±5 | 900±300 | ＜0.1% | ＞99.0 | In the field of aspartic polyurea tile grout, at 25 ℃，50% RH, the working time for the product is 20-25 minutes,the trimming time is shorten to 2-3h,engough operation time and the curing speed in the later period is fast. | |
| N5631 | NCO content（%） | Viscosity（Pa·s@25℃） | Water（%） | effective constituent（%） | |
| 15.0±0.5% | 4500±500 | — | ＞99% | ||
| Products can be customized according to the specific needs of customers | |||||
| Aspartic polyurea sealant raw material recommended solution | |||||
|---|---|---|---|---|---|
| A, B component 1:1 ratio | |||||
| T7400 | Total amine value mgKOH/g | Viscosity（mPa·s@25℃） | Water（%） | solid content（%） | Characteristics and applications In the field of aspartic polyurea caulking glue, at 25 ℃，50% RH,the tack free time of the product is 3~4h, good adhesion to cement, glazed ceramics and other substrates. |
| 51±5 | 1100±300 | ＜0.1 | ＞99.0 | ||
| N6030 | NCO content（%） | Viscosity（mPa·s@25℃） | Water（%） | effective constituent（%） | |
| 4±0.5% | 6400±500 | — | ＞99.0 | ||
| A, B component 1:1 ratio | |||||
| T7100 | Total amine value mgKOH/g | Viscosity（mPa·s@25℃） | Water（%） | solid content（%） | In the field of aspartic polyurea cosmetic adhesives, at 25 ℃，50% RH,the product tack-free time is 2-3h. It has good adhesion and flexibility at ultra-low temperatures of -20℃, and has excellent adhesion on substrates such as cement, glass, and glazed ceramics. |
| 51±5 | 1200±300 | ＜0.1 | ＞99.0 | ||
| N2030 | NCO content（%） | Viscosity（mPa·s@25℃） | Water（%） | effective constituent（%） | |
| 4±0.5 | 3800±500 | — | ＞99.0 | ||
| A、B component 1:3 ratio | |||||
| B3700 | Total amine value mgKOH/g | Viscosity（mPa·s@25℃） | Water（%） | solid content（%） | In the field of aspartic polyurea caulking glue, at 25 ℃，50% RH, the tack free time of the product is 4~5h, the operation time is sufficient, good adhesion to cement, glass, glazed ceramics and other substrates. |
| 97±5 | 6800±500 | ＜0.1 | ＞99.0 | ||
| N6031 | NCO content（%） | Viscosity（mPa·s@25℃） | Water（%） | effective constituent（%） | |
| 4±0.5 | 1700±500 | — | ＞99.0 | ||
| Aspartic polyurea coating raw material recommended solution | |||||
|---|---|---|---|---|---|
| Product grades | Product parameters | Characteristics and applications | |||
| General aspartic waterproofing coating | |||||
| P4001 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Super weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion; Classic data of finished products: at 23℃，50%RH，working time 30min, tack free time 45min, hard dry time 4h, tensile strength 20MPa, elongation at break 150%.The mass ratio or volume ratio can both be achieved in a 1:1 ratio. Recommended applications: water park, roof, hospital and other light load elastic floor, building repair, metal protective paint, rail transit waterproof |
| 195±10 | 950±300 | ＜0.1 | ＞97.0 | ||
| N5561 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 6.6±0.5 | 3100±500 | — | ＞85.0 | ||
| Low elastic aspartic coating | |||||
| Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather-resistant, chemicals-resistant, wear-resistant, good mechanical properties, good adhesion; Classic data of finished products: at 23℃, 50% RH, working time 30 minutes, tack free time 60 minutes, hard dry time 8 hours, tensile strength 15 MPa, elongation at break 150%. The ratio of mass or volume can be 1:1. Recommended applications: waterproofing and repair in roofing, construction, rail transit waterproofing. |
|
| P4001 | 195±10 | 950±300 | ＜0.1 | ＞97.0 | |
| N5562 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 6.1±0.5 | 3000±500 | — | ＞85.0 | ||
| High elastic aspartic coating | |||||
| C4255 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Super weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion; Classic data of finished products: 23℃，50%RH, working time 30min, tack free time 45min, hard dry time 6h, tensile strength 20MPa, elongation at break 500%. Recommended applications: waterproofing of hydraulic dam body, wear-resistant surface of plastic runway, waterproofing repair, wind power front protective coating. |
| 222±10 | 260±100 | ＜0.1 | ＞97.0 | ||
| N6671 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 3.5±0.5 | 2500±500 | — | ＞73.0 | ||
| Fast drying aspartic floor coating（It can be made into finished transparent coating according to the ratio 1:1） | |||||
| P4003 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion; Classic data of finished products: 23℃，50%RH，working time 30min, hard dry time 8h, tensile strength 25MPa, elongation 10%，1 day the hardness can achieve to 70D.The ratio of mass or volume can be 1:1. Recommended application: colored flake floor spreading base coat and top coat. |
| 170±10 | 300±200 | ＜0.1 | ＞85.0 | ||
| N5050 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 13.0±0.5 | 500±300 | — | ＞85.0 | ||
| Slow drying aspartic floor coating（It can be made into finished transparent coating according to the ratio 1:1） | |||||
| P5001 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather-resistant, chemical- resistant, wear-resistant, good mechanical properties, good adhesion; Classic data of finished products: at 23℃, 50% RH, working time 120 minutes, hard dry time 24 hours, hardness 70D after 4 days. Recommended applications: self-leveling, garage flooring, etc. |
| 195±10 | 1000±300 | ＜0.1 | ＞85.0 | ||
| N5050 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 13.0±0.5 | 500±300 | — | ＞85.0 | ||
| Solvent free aspartic floor coating （It can be made into finished transparent coating according to the ratio 1:1） | |||||
| P4004 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather-resistant, chemical- resistant, wear-resistant, good mechanical properties, good adhesion; Classic data of finished products: at 23℃, 50% RH, working time 35minutes, hard dry time 24 hours, hardness 70D after 2days. Recommended applications: general used floor top coating.Including the maintenance of kitchen and bathroom etc. |
| 170±10 | 500±300 | ＜0.1 | ＞98.0 | ||
| N5051 | NC content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 13.0±0.5 | 900±300 | — | ＞98.0 | ||
| protective gelcoat | |||||
| C4602 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion; Classic data of finished products: 23℃，50%RH, working time 90min, tack free time 30min, hard dry time 8h, pencil hardness > H. Recommended application: Protective coating for outdoor used composite material pipes, plates, etc. |
| 277±10 | 500±200 | ＜0.1 | ＞97.0 | ||
| N4091 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 20.5±0.5 | 700±300 | — | ＞90.0 | ||
| High rebound aspartic thin film coating（ Mix to use according to the ratio of 1:2） | |||||
| C4005 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather-resistant, chemically resistant, wear-resistant, high elasticity and strength, good adhesion; Finished product classic datas: 23℃，50%RH, life in the tank is 90 minutes, tack free time 30 minutes, hard dry time 5 hours. The tensile strength is 30MPa，elongation at break 500%。 Recommended application：Aspartic sparying car cover intermediate coating, glass anti-shatter film, shoe sole foam protective coating. |
| 106±10 | 300±200 | ＜0.1 | ＞50.0 | ||
| N7955 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 3.5±0.5 | 300±200 | — | ＞50.0 | ||
| DTM anti-corrosion topcoat | |||||
| C4001 | Total amine value mgKOH/g | Viscosity mPa·s@25℃ | Water % | Solid content % | Weather-resistant, chemical-resistant, wear-resistant, with good adhesion; Finished product classic datas:23℃,50%rh,tack free time 60min，hard dry time 4h;pencil hardness 2H. Recommended application:Steel structure anti-corrosion topcoat, DTM anti-corrosion coating. |
| 195±10 | 950±300 | ＜0.1% | ＞97.0 | ||
| N9100 | NCO content % | Viscosity mPa·s@25℃ | Water % | Effective constituent（%） | |
| 15.3±0.5 | 300±200 | — | ＞90.0 | ||