Aspartic polyurea coating raw material recommended solution
Product grades Product parameters Characteristics and applications
General aspartic waterproofing coating
P4001 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Super weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion;
Classic data of finished products: at 23℃,50%RH, working time 30min, tack free time 45min, hard dry time 4h, tensile strength 20MPa, elongation at break 150%.The mass ratio or volume ratio can both be achieved in a 1:1 ratio.
Recommended applications: water park, roof, hospital and other light load elastic floor, building repair, metal protective paint, rail transit waterproof
195±10 950±300 ＜0.1 ＞97.0
N5561 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
6.6±0.5 3100±500 — ＞85.0
Low elastic aspartic coating
Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather-resistant, chemicals-resistant, wear-resistant, good mechanical properties, good adhesion;
Classic data of finished products: at 23℃, 50% RH, working time 30 minutes, tack free time 60 minutes, hard dry time 8 hours, tensile strength 15 MPa, elongation at break 150%. The ratio of mass or volume can be 1:1.
Recommended applications: waterproofing and repair in roofing, construction, rail transit waterproofing.
P4001 195±10 950±300 ＜0.1 ＞97.0
N5562 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
6.1±0.5 3000±500 — ＞85.0
High elastic aspartic coating
C4255 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Super weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion;
Classic data of finished products: 23℃,50%RH, working time 30min, tack free time 45min, hard dry time 6h, tensile strength 20MPa, elongation at break 500%.
Recommended applications: waterproofing of hydraulic dam body, wear-resistant surface of plastic runway, waterproofing repair, wind power front protective coating.
222±10 260±100 ＜0.1 ＞97.0
N6671 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
3.5±0.5 2500±500 — ＞73.0
Fast drying aspartic floor coating (It can be made into finished transparent coating according to the ratio 1:1)
P4003 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion;
Classic data of finished products: 23℃,50%RH, working time 30min, hard dry time 8h, tensile strength 25MPa, elongation 10%, 1 day the hardness can achieve to 70D.The ratio of mass or volume can be 1:1.
Recommended application: colored flake floor spreading base coat and top coat.
170±10 300±200 ＜0.1 ＞85.0
N5050 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
13.0±0.5 500±300 — ＞85.0
Slow drying aspartic floor coating (It can be made into finished transparent coating according to the ratio 1:1)
P5001 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather-resistant, chemical-resistant, wear-resistant, good mechanical properties, good adhesion;
Classic data of finished products: at 23℃, 50% RH, working time 120 minutes, hard dry time 24 hours, hardness 70D after 4 days.
Recommended applications: self-leveling, garage flooring, etc.
195±10 1000±300 ＜0.1 ＞85.0
N5050 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
13.0±0.5 500±300 — ＞85.0
Solvent free aspartic floor coating (It can be made into finished transparent coating according to the ratio 1:1)
P4004 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather-resistant, chemical-resistant, wear-resistant, good mechanical properties, good adhesion;
Classic data of finished products: at 23℃, 50% RH, working time 35minutes, hard dry time 24 hours, hardness 70D after 2days.
Recommended applications: general used floor top coating. Including the maintenance of kitchen and bathroom etc.
170±10 500±300 ＜0.1 ＞98.0
N5051 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
13.0±0.5 900±300 — ＞98.0
protective gelcoat
C4602 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather resistance, chemical resistance, wear resistance, good mechanical properties, good adhesion;
Classic data of finished products: 23℃,50%RH, working time 90min, tack free time 30min, hard dry time 8h, pencil hardness > H.
Recommended application: Protective coating for outdoor used composite material pipes, plates, etc.
277±10 500±200 ＜0.1 ＞97.0
N4091 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
20.5±0.5 700±300 — ＞90.0
High rebound aspartic thin film coating ( Mix to use according to the ratio of 1:2)
C4005 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather-resistant, chemically resistant, wear-resistant, high elasticity and strength, good adhesion;
Finished product classic datas: 23℃,50%RH, life in the tank is 90 minutes, tack free time 30 minutes, hard dry time 5 hours.
The tensile strength is 30MPa, elongation at break 500%.
Recommended application：Aspartic sparying car cover intermediate coating, glass anti-shatter film, shoe sole foam protective coating.
106±10 300±200 ＜0.1 ＞50.0
N7955 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
3.5±0.5 300±200 — ＞50.0
DTM anti-corrosion topcoat
C4001 Total amine value mgKOH/g Viscosity mPa·s@25℃ Water % Solid content % Weather-resistant, chemical-resistant, wear-resistant, with good adhesion;
Finished product classic datas:23℃,50%rh, tack free time 60min, hard dry time 4h; pencil hardness 2H.
Recommended application: Steel structure anti-corrosion topcoat, DTM anti-corrosion coating.
195±10 950±300 ＜0.1% ＞97.0
N9100 NCO content % Viscosity mPa·s@25℃ Water % Effective constituent %
15.3±0.5 300±200 — ＞90.0